Passes: 24 x 0.25mm

Power: 100%

Speed: 0.2 - 2.0 mm/s

Samples: 4 x 10

Startheight: 68

Offset: -5

Collection: 

The cut quality seems to have diminished at the higher speeds, but no drastically.

Top left tripple is last clean trio. Will test heart at 1.4

-19

-16

Passes: 32 x 0.25mm

Power: 100%

Speed: 2.1 - 3.2 mm/s

Samples: 7 x 11

Startheight: 68

Offset: -3

Slice was very thick, so we had to reduce offset.

Mill bit seems to have snapped at 2.1/2.2 mm/s

Collection: 

-16

-13

-19

-15

Passes: 24 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 21

Startheight: 68

Offset: -5

Spindle didnt start. Will retry the rest

-12

-8

-14

-10

Passes: 24 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 21

Startheight: 68

Offset: -5

Collection: 

I suspect the delay that happends while moving the collector is interferring with the python code recieving plotting data over serial.

-13

-8

-16

-13

Passes: 24 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 68

Offset: -5

Collection: 

Samples hitting sample tube: 

-12

-10

https://youtu.be/j_wQHvgTn18

https://youtu.be/HizZnf6zzcs

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 68

Offset: -3

Sample was very thick and thus required more passes and lower starting depth.

Spindle needed help starting, and then needed some time "warmin up".

Collection: 

Samples hitting sample tube: 

-16

-11

-17

-14

https://youtu.be/gbdpPS3zblo

https://youtu.be/WKYoWSt7mcY

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 68

Offset: -3

Spindle needed much help starting

Collection: 

Samples hitting sample tube: 

-12

-6

-13

-11

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Spindle needed much help starting

Switched between height difference in startheight and offset, to not crash into spooning as in test 6.

Collection: 

Samples hitting sample tube: 

-10

-3

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Collection: 

Samples hitting sample tube: 

-17

-14

-18

-15

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Collection: 

Samples hitting sample tube: 

-12

-6

-13

-11

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Collection: 

Samples hitting sample tube: 

-11

-8

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Mill bit snapped on sample 1. Need to inspect video to find where exactly. I suspect it had to do with frost on the mill bit head.

Collection: 

Samples hitting sample tube: 

-20

-17

-20

-17

1:02:59

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Collection: 

Samples hitting sample tube: 

-14

-11

-16

-13

Passes: 32 x 0.25mm

Power: 100%

Speed: 1,4 mm/s

Samples: 6

Startheight: 66

Offset: -5

Collection: 

Samples hitting sample tube: 

-8

-1

-12

-10