Strength testing
| Test | Slice | Time | Settings | Status | Comment | Image slice | Image samples | Start temp | End temp | Video | ||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 1 | 1 | 3:40:59 | Passes: 24 x 0.25mm Power: 100% Speed: 0.2 - 2.0 mm/s Samples: 4 x 10 Startheight: 68 Offset: -5 | Success | Collection:
The cut quality seems to have diminished at the higher speeds, but no drastically. Top left tripple is last clean trio. Will test heart at 1.4 |
|
| -19 -16 | https://youtu.be/Q7-xXIwxTPM | |||||
| 2 | 2 | 3:38:52 | Passes: 32 x 0.25mm Power: 100% Speed: 2.1 - 3.2 mm/s Samples: 7 x 11 Startheight: 68 Offset: -3 | Failed | Slice was very thick, so we had to reduce offset. Mill bit seems to have snapped at 2.1/2.2 mm/s Collection:
|
| -16 -13 | -19 -15 | ||||||
| 3 | 3 | 1:32:52 | Passes: 24 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 21 Startheight: 68 Offset: -5 | Failed | Spindle didnt start. Will retry the rest | -12 -8 | -14 -10 | https://youtu.be/PJDutBnNRKY | ||||||
| 4 | 3 | 2:32:09 | Passes: 24 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 21 Startheight: 68 Offset: -5
| Success | Collection:
I suspect the delay that happends while moving the collector is interferring with the python code recieving plotting data over serial. |
|
| -13 -8 | -16 -13 | https://youtu.be/6xy1UvTddZ0 |
Confirmatory testing
| Test | Slice | Time | Settings | Status | Comment | Image slice | Image samples | Start temp | End temp | Video | |||||||||||||||||||||||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| 5 | 4 | 47:45 | Passes: 24 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 68 Offset: -5 | Success | Collection:
Samples hitting sample tube:
|
|
| -12 -10 | |||||||||||||||||||||||||||
| 6 | 5 | 1:02:34 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 68 Offset: -3 | Success | Sample was very thick and thus required more passes and lower starting depth. Collection:
Samples hitting sample tube:
|
|  
| -16 -11 | -17 -14 | ||||||||||||||||||||||||||
| 7 | 6 | 1:02:34 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 68 Offset: -3
| Success | Spindle needed much help starting Collection:
Samples hitting sample tube:
|
|
| -12 -6 | -13 -11 | https://youtu.be/HJW80P2nLXs | |||||||||||||||||||||||||
| 8 | 7 | 1:02:50 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5
| Success | Spindle needed much help starting
Collection:
Samples hitting sample tube:
|
|
| -10 -3 | https://youtu.be/8nd7U2SRzIo | ||||||||||||||||||||||||||
| 9 | 8 | 1:02:50 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5 | Success | Collection:
Samples hitting sample tube:
|
| 
| -17 -14 | -18 -15 | https://youtu.be/llPHwaFFM_s | |||||||||||||||||||||||||
| 10 | 9 | 1:02:50 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5 | Success | Collection:
Samples hitting sample tube:
|
| 
| -12 -6 | -13 -11 | https://youtu.be/wRDkFWP-q90 | |||||||||||||||||||||||||
| 11 | 10 | N/A | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5 | Success | Collection:
Samples hitting sample tube:
|
|
| -11 -8 | https://youtu.be/4FcApJBjscM | ||||||||||||||||||||||||||
| 12 | 11 | 21:45 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5 | Failure | Mill bit snapped on sample 1. Need to inspect video to find where exactly. I suspect it had to do with frost on the mill bit head. Collection:
Samples hitting sample tube:
|
| -20 -17 | -20 -17 | |||||||||||||||||||||||||||
| 13 | 11 | 1:02:59 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5 | Success | Collection:
Samples hitting sample tube:
|
| 
| -14 -11 | -16 -13 | ||||||||||||||||||||||||||
| 14 | 12 | 1:03:02 | Passes: 32 x 0.25mm Power: 100% Speed: 1,4 mm/s Samples: 6 Startheight: 66 Offset: -5 | Success | Collection:
Samples hitting sample tube:
|
| 
| -8 -1 | -12 -10 |