Passes: 10 x 0.5mm
Power: 100%
Speed: 0.2 - 2.3 mm/s
Samples: 3 x 22
Startheight: 68
Mill bit broke on sample 2 of 0.4 mm/s
Fracture probably happened during pass transition at 01:24:25.
Seems samples need more spaceing, since tissue is softer. Current spacing is 1 mm.
All samples at 0.3mm/s did not completely detach from the slice.
Collection:
| Dropping | Did not fall |
|---|---|
| 2 | 5 |
- Review video
Samples hitting sample tube:
| Hit 1 | 4 |
|---|---|
| Miss 1 | 2 |
-16
-14
-18
-16
Passes: 20 x 0.25mm
Power: 100%
Speed: 0.2 - 0.7 mm/s
Samples: 3 x 6
Startheight: 68
Collection:
| Dropping | Did not fall |
|---|---|
| 17 | 1 |
Samples hitting sample tube:
| Hit 1 | 5 |
|---|---|
| Miss 1 | 12 |
-10
-5
-26
-25
Passes: 20 x 0.25mm
Power: 100%
Speed: 0.8 - 2.2 mm/s
Samples: 3 x 15
Startheight: 68
Mill bit broke on sample 1 of 1.9 mm/s
Collection:
| Dropping | Did not fall |
|---|---|
| 27 | 6 |
Samples hitting sample tube:
| Hit 1 | 15 |
|---|---|
| Miss 1 | 12 |
-17
-11
-19
-16
Passes: 20 x 0.25mm
Power: 100%
Speed: 1.7 mm/s
Samples: 45
Startheight: 68
Offset: -6 (same as every test before)
Mill bit broke on sample 8 on first pass
- The right side of the slice becomes raised at 20:40 - 20:45 because of too little support from the arms. This caused the first pass of sample 8 to be too deep.
Collection:
| Dropping | Did not fall |
|---|---|
| 2 | 5 |
Samples hitting sample tube:
| Hit 1 | 1 |
|---|---|
| Miss 1 | 1 |
-13
-10
-14
-12
Passes: 24 x 0.25mm
Power: 100%
Speed: 1.1 - 1.7 mm/s
Samples: 8 x 7
Startheight: 68
Offset: -5
Collection:
| Dropping | Did not fall | |
|---|---|---|
| 1.1 | 8 | 0 |
| 1.2 | 8 | 0 |
| 1.3 | 8 | 0 |
| 1.4 | 8 | 0 |
| 1.5 | 8 | 0 |
| 1.6 | 7 | 1 |
| 1.7 | 7 | 1 |
The cut quality seems higher on 1.1 mm/s than 1.7. Even though the mill bit did not break i would recommend max speed at 1.3 mm/s.
Samples hitting sample tube:
| Hit 1 | 26 |
|---|---|
| Miss 1 | 28 |
-12
-11
-17
-14