Breakdown Voltage of Polymeric HVDC Insulation at DC Stress and Superimposed Lightning Impulse Voltages
DOI:
https://doi.org/10.5324/nordis.v27i1.4918Sammendrag
Space charge formation makes it difficult to predict the resulting electric field distribution within HVDC cable insulation.
The main purpose of the work presented here has been to experimentally study how the lightning impulse breakdown strength of thin (0.1 mm thick) insulation foils of polypropylene (PP) and Polyethylene Terephthalate (PET) are affected by DC prestress, polarity of the impulse voltage and the temperature.
Tests were performed using parallel plate electrodes and prior to DC prestressing the lightning impulse breakdown strengths were found to be approximately 17.5 kV for samples of both PP and PET. Prior to superimposing lightning impulse breakdown voltages, a DC voltage of 8 kV was applied for 60 seconds. The effect of DC prestressing was to significantly increase the impulse breakdown strength during aiding and reduce the breakdown strength during opposing impulse polarity. This strongly support the assumption of homo-charge formation close to the metal electrodes during DC stress.
The results showed higher and more temperature dependent charge accumulation in samples of PET. It is indicated that at 22 °C the homo-charge formed during DC stressing approximately reduced the electric field at the electrodes from 100 to 48 kV/mm in the PP samples and from 80 to 22 kV/mm in the PET samples, respectively
Downloads
Nedlastinger
Publisert
Utgave
Seksjon
Lisens
Opphavsrett 2022 Erling Ildstad; Frank Mauseth; Espen T. Olsen
Dette verket er lisensiert under en Creative Commons Attribution 4.0 International Lisens.
Proceedings of the Nordic Insulation Symposium licenses all content of the journal under a Creative Commons Attribution (CC-BY) licence. This means, among other things, that anyone is free to copy and distribute the content, as long as they give proper credit to the author(s) and the journal. For further information, see Creative Commons website for human readable or lawyer readable versions.
Authors who publish with this journal agree to the following terms:
1. Authors retain copyright and grant the journal right of first publication with the work simultaneously licensed under a Creative Commons Attribution License that allows others to share the work with an acknowledgement of the work's authorship and initial publication in this journal.
2. Authors are able to enter into separate, additional contractual arrangements for the non-exclusive distribution of the journal's published version of the work (e.g., post it to an institutional repository or publish it in a book), with an acknowledgement of its initial publication in this journal.
3. Authors are permitted and encouraged to post their work online (e.g., in institutional repositories or on their website) prior to and during the submission process, as it can lead to productive exchanges, as well as earlier and greater citation of published work (See The Effect of Open Access).